TRILOY® TP270W

PC/ABS

Inquiry

TYPICAL DATA OF TRILOY® TP270W GRADE

PROPERTY UNIT ASTM METHOD TYPICAL DATA
Physical
Specific Gravity - D792 1.34
Water Absorption (24 hours at 23℃) % D570 0.2
Melt Flow Rate (260℃, 2.16kg) g/10min D1238 40
MECHANICAL
Tensile Strength at yield kgf/㎠ D638 500
Tensile Elongation at break % D638 4
Flexural Strength at yield kgf/㎠ D790 800
Flexural Modulus kgf/㎠ D790 42,000
Izod Impact Strength, notched, 23℃ (1/8”) kgf∙㎝/㎝ D256 3
THERMAL
HDT, 18.6 ㎏f/㎠ D648 82
ELECTRICAL
OTHERS
UL-94 Flammability (1.4mm thickness) - (UL 94) V-0
※The figures listed in this table are typical values obtained under the standard test methods and may not be applicable for products that are under different application condition.

PROCESSING GUIDE FOR TRILOY® TP270W GRADE

General processing conditions for TRILOY® TP270W are shown below.
Drying prior to processing is essential to ensure desired appearance and property performance.

SPECIFICATION UNIT CONDITIONS
Drying Temperature 70~80
Drying Time hr 4~6
Moisture Content, Max % 0.02
Melt Temperature 250~270
Nozzle Temperature 250~260
Front Temperature 250~260
Middle Temperature 245~265
Rear Temperature 230~250
Mold Temperature 40~60
Back Pressure MPa 0.4~0.6
Screw Speed rpm 50~60
Vent Depth mm 0.02~0.08
Injection Pressure MPa 50~80
Injection Speed % 20~50
Hold Pressure MPa 35~60
Injection Cushion mm 3~6