TRICAP® OG44S

Organosheet

Inquiry

TYPICAL DATA OF TRICAP® OG44S GRADE

PROPERTY UNIT TYPICAL DATA
Material - PA6 GF(Satin)
Fiber Contents Vol % 40
Specific Gravity - 1.7
Tensile Strength MPa 362
Tensile Modulus GPa 19
Flexural Strength MPa 282
Flexural Modulus GPa 16.3
Note -
※The figures listed in this table are typical values obtained under the standard test methods and may not be applicable for products that are under different application condition.

PROCESSING GUIDE FOR TRICAP® OG44S GRADE

Heating

  • Between 200℃ ~ 250℃
  • We recommend molding in the above temperature range for good impregnation performance and forming. It is recommended to use middle wavelength IR heater for heating heat source. Two-sided heating will be much more efficient than one side.

Pressing

  • 10 ~ 100 bar
  • The impregnation pressure may vary depending on the molded part, shape and molding tool.

Demolding Temperature

  • Under 100℃
  • It is recommended to demold at the lowest temperature possible to avoid deforming the shape during demolding process.

Dimensions

  • Precut on demand Plate, size 640mm × 600mm

Storage

  • The storage time of the Organosheet is infinite.

Handling

  • PA is stable at room temperature and normal pressure. In order to manufacture molded parts using Organosheet, you need a special safety guard and tools.