TYPICAL DATA OF TRICAP® OG14T GRADE
| PROPERTY | UNIT | TYPICAL DATA |
|---|---|---|
| Material | - | PP GF(Twill) |
| Fiber Contents | Vol % | 43.5 |
| Specific Gravity | - | 1.62 |
| Tensile Strength | MPa | 420 |
| Tensile Modulus | GPa | 18.5 |
| Flexural Strength | MPa | 430 |
| Flexural Modulus | GPa | 18 |
| Note | - |
※The figures listed in this table are typical values obtained under the standard test methods and may not be applicable for products that are under different application condition.
PROCESSING GUIDE FOR TRICAP® OG14T GRADE
Heating
- Between 200℃ ~ 250℃
- We recommend molding in the above temperature range for good impregnation performance and forming. It is recommended to use middle wavelength IR heater for heating heat source. Two-sided heating will be much more efficient than one side.
Pressing
- 10 ~ 100 bar
- The impregnation pressure may vary depending on the molded part, shape and molding tool.
Demolding Temperature
- Under 100℃
- It is recommended to demold at the lowest temperature possible to avoid deforming the shape during demolding process.
Dimensions
- Precut on demand Plate, max size 600mm × 1500mm
Storage
- The storage time of the Organosheet is infinite.
Handling
- PP is stable at room temperature and normal pressure. In order to manufacture molded parts using Organosheet, you need a special safety guard and tools.