TYPICAL DATA OF TRIEL® HV5401BH GRADE
PROPERTY | UNIT | ASTM METHOD | TYPICAL DATA |
---|---|---|---|
Physical | |||
Specific Gravity | - | D792 | 1.15 |
Water Absorption (24 hours at 23℃) | % | D570 | 0.5 |
Melt Flow Rate (230℃, 2.16kg) | g/10min | D1238 | 1 |
Melt Flow Rate (230℃, 10kg) | g/10min | 7 | |
MECHANICAL | |||
Tensile Strength at yield | kgf/㎠ | D638 | 110(@50%) |
Tensile Elongation at break | % | D638 | >600 |
Flexural Strength at yield | kgf/㎠ | D790 | 58 |
Izod Impact Strength, notched, 23℃ (1/8”) | kgf∙㎝/㎝ | D256 | No Break |
Hardness (Shore D) | Shore D | 45 | |
THERMAL | |||
HDT, 4.6 ㎏f/㎠ | ℃ | 56 | |
Vicat softening temperature | ℃ | 155 | |
ELECTRICAL | |||
OTHERS | |||
Mold Shrinkage (3mm thickness) | % | D955 | 1.5~1.7 |
※The figures listed in this table are typical values obtained under the standard test methods and may not be applicable for products that are under different application condition.
PROCESSING GUIDE FOR TRIEL® HV5401BH GRADE
General processing conditions for TRIEL® HV5401BH are shown below.
Drying prior to processing is essential to ensure desired appearance and property performance.
SPECIFICATION | UNIT | CONDITIONS |
---|---|---|
Drying Temperature | ℃ | 100~110 |
Drying Time | hr | 3~4 |
Moisture Content, Max | % | 0.02 |
Melt Temperature | ℃ | 220~250 |
Nozzle Temperature | ℃ | 220~250 |
Front Temperature | ℃ | 220~250 |
Middle Temperature | ℃ | 220~250 |
Rear Temperature | ℃ | 200~220 |
Mold Temperature | ℃ | 30~50 |
Back Pressure | MPa | 0.0~0.1 |
Screw Speed | rpm | 10~50 |
Vent Depth | mm | 0.02~0.08 |