Inquiry

TYPICAL DATA OF TRIEL® 5551BM GRADE

PROPERTY UNIT ASTM METHOD TYPICAL DATA
Physical
Specific Gravity - D792 1.22
Water Absorption (24 hours at 23℃) % D570 0.5
Melt Flow Rate (230℃, 2.16kg) g/10min D1238 0.5
Melt Flow Rate (230℃, 10kg) g/10min 5
MECHANICAL
Tensile Strength at yield kgf/㎠ D638 270
Tensile Elongation at break % D638 >400
Flexural Strength at yield kgf/㎠ D790 70
Flexural Modulus kgf/㎠ D790 1,200
Izod Impact Strength, notched, 23℃ (1/8”) kgf∙㎝/㎝ D256 No Break
Hardness (Shore D) Shore D 55
THERMAL
HDT, 4.6 ㎏f/㎠ 86
Vicat softening temperature 174
ELECTRICAL
OTHERS
Mold Shrinkage (3mm thickness) % D955 1.5~2.0
※The figures listed in this table are typical values obtained under the standard test methods and may not be applicable for products that are under different application condition.

PROCESSING GUIDE FOR TRIEL® 5551BM GRADE

General processing conditions for TRIEL® 5551BM are shown below.
Drying prior to processing is essential to ensure desired appearance and property performance.

SPECIFICATION UNIT CONDITIONS
Drying Temperature 100~110
Drying Time hr 3~4
Moisture Content, Max % 0.02
Melt Temperature 200~230
Nozzle Temperature 200~230
Front Temperature 200~230
Middle Temperature 200~230
Rear Temperature 180~200
Mold Temperature 30~50
Back Pressure MPa 0.0~0.1
Screw Speed rpm 10~50
Vent Depth mm 0.02~0.08