TYPICAL DATA OF TRAMID® 4210GNH30 GRADE
PROPERTY | UNIT | ASTM METHOD | TYPICAL DATA |
---|---|---|---|
Physical | |||
Specific Gravity | - | D792 | 1.40 |
MECHANICAL | |||
Tensile Strength at yield | kgf/㎠ | D638 | 125 |
Tensile Elongation at break | % | D638 | > 1.8 |
Flexural Strength at yield | kgf/㎠ | D790 | 185 |
Flexural Modulus | kgf/㎠ | D790 | 9,000 |
Izod Impact Strength, notched, 23℃ (1/8”) | kgf∙㎝/㎝ | D256 | 55 |
THERMAL | |||
HDT, 18.6 ㎏f/㎠ | ℃ | D648 | 235 |
ELECTRICAL | |||
Dielectric Constant | - | D150 | 4.0 |
OTHERS | |||
UL-94 Flammability (0.75, 1.5, 3.0mm) | - | (UL 94) | V-0 |
Mold Shrinkage | % | 0.3~0.8 |
※The figures listed in this table are typical values obtained under the standard test methods and may not be applicable for products that are under different application condition.
PROCESSING GUIDE FOR TRAMID® 4210GNH30 GRADE
General processing conditions for TRAMID® 4210GNH30 are shown below.
Drying prior to processing is essential to ensure desired appearance and property performance.
SPECIFICATION | UNIT | CONDITIONS |
---|---|---|
Drying Temperature | ℃ | 80~100 |
Drying Time | hr | 4~6 |
Melt Temperature | ℃ | 270~290 |
Nozzle Temperature | ℃ | 270~290 |
Front Temperature | ℃ | 270~290 |
Middle Temperature | ℃ | 260~280 |
Rear Temperature | ℃ | 240~260 |
Mold Temperature | ℃ | 60~100 |
Back Pressure | MPa | <70 |
Screw Speed | rpm | <60 |
Injection Pressure | MPa | <70 |
Injection Speed | % | <60 |
Hold Pressure | MPa | <50 |
Injection Cushion | mm | 3~6 |