TRIREX® 3025G10

PC

Inquiry

TYPICAL DATA OF TRIREX® 3025G10 GRADE

PROPERTY UNIT ASTM METHOD TYPICAL DATA
Physical
Specific Gravity - D792 1.25
Water Absorption (24 hours at 23℃) % D570 0.13
Melt Flow Rate (300℃, 1.2kg) g/10min D1238 10
MECHANICAL
Tensile Strength at yield kgf/㎠ D638 800
Tensile Elongation at break % D638 10
Flexural Strength at yield kgf/㎠ D790 1,300
Flexural Modulus kgf/㎠ D790 37,000
Izod Impact Strength, notched, 23℃ (1/8”) kgf∙㎝/㎝ D256 12
Rockwell Hardness R scale D785 121
THERMAL
HDT, 18.6 ㎏f/㎠ D648 140
ELECTRICAL
Volume Resistivity Ω∙㎝ D257 4E+16
Dielectric Strength kV/㎜ D149 31
Dielectric Constant - D150 2.97
Dissipation Factor - D150 0.0096
ARC Resistance sec D495 120
OTHERS
UL-94 Flammability (1.5mm thickness) - (UL 94) V-0
Mold Shrinkage (3mm thickness) % D955 0.3~0.5
※The figures listed in this table are typical values obtained under the standard test methods and may not be applicable for products that are under different application condition.

PROCESSING GUIDE FOR TRIREX® 3025G10 GRADE

General processing conditions for TRIREX® 3025G10 are shown below.
Drying prior to processing is essential to ensure desired appearance and property performance.

SPECIFICATION UNIT CONDITIONS
Drying Temperature 120
Drying Time hr 3~4
Moisture Content, Max % 0.02
Melt Temperature 290~310
Nozzle Temperature 300~320
Front Temperature 300~320
Middle Temperature 290~310
Rear Temperature 280~300
Mold Temperature 80~110