TRILOY® 200

PC/ABS

Inquiry

TYPICAL DATA OF TRILOY® 200 GRADE

PROPERTY UNIT ASTM METHOD TYPICAL DATA
Physical
Specific Gravity - D792 1.08
Water Absorption (24 hours at 23℃) % D570 0.2
Melt Flow Rate (250℃, 5kg) g/10min D1238 17
MECHANICAL
Tensile Strength at yield kgf/㎠ D638 500
Tensile Elongation at break % D638 100
Flexural Strength at yield kgf/㎠ D790 700
Flexural Modulus kgf/㎠ D790 23,000
Izod Impact Strength, notched, 23℃ (1/8”) kgf∙㎝/㎝ D256 50
Rockwell Hardness R scale D785 100
THERMAL
HDT, 18.6 ㎏f/㎠ D648 100
Coefficient of Linear Thermal Expansion ㎜/㎜/℃ D696 7.3 x 10-5
ELECTRICAL
Volume Resistivity Ω∙㎝ D257 5E+16
Dielectric Strength kV/㎜ D149 25
Dielectric Constant - D150 3
Dissipation Factor - D150 0.009
ARC Resistance sec D495 123
OTHERS
UL-94 Flammability (1.5mm thickness) - (UL 94) HB
Mold Shrinkage (3mm thickness) % D955 0.5~0.7
※The figures listed in this table are typical values obtained under the standard test methods and may not be applicable for products that are under different application condition.

PROCESSING GUIDE FOR TRILOY® 200 GRADE

General processing conditions for TRILOY® 200 are shown below.
Drying prior to processing is essential to ensure desired appearance and property performance.

SPECIFICATION UNIT CONDITIONS
Drying Temperature 60~90
Drying Time hr 3~5
Moisture Content, Max % 0.02
Melt Temperature 240~270
Nozzle Temperature 245~255
Front Temperature 250~260
Middle Temperature 250~260
Rear Temperature 240~250
Mold Temperature 60~90