TRIEL® PZ5063SP

TPEE

Inquiry

TYPICAL DATA OF TRIEL® PZ5063SP GRADE

PROPERTY UNIT ASTM METHOD TYPICAL DATA
Physical
Specific Gravity - D792 1.07
Water Absorption (24 hours at 23℃) % D570 0.5
Melt Flow Rate (190℃, 2.16kg) g/10min D1238 18.0
MECHANICAL
Tensile Strength at yield kgf/㎠ D638 70.0
Tensile Elongation at break % D638 >400
Flexural Strength at yield kgf/㎠ D790 20.0
Flexural Modulus kgf/㎠ D790 32.0
Izod Impact Strength, notched, 23℃ (1/8”) kgf∙㎝/㎝ D256 No Break
THERMAL
ELECTRICAL
OTHERS
Mold Shrinkage % 1.5
※The figures listed in this table are typical values obtained under the standard test methods and may not be applicable for products that are under different application condition.

PROCESSING GUIDE FOR TRIEL® PZ5063SP GRADE

General processing conditions for TRIEL® PZ5063SP are shown below.
Drying prior to processing is essential to ensure desired appearance and property performance.

SPECIFICATION UNIT CONDITIONS
Drying Temperature 80~90
Drying Time hr 2~3
Moisture Content, Max % 0.02
Melt Temperature 150~160
Nozzle Temperature 180~200
Front Temperature 180~200
Middle Temperature 180~200
Rear Temperature 160~180
Mold Temperature 30~50
Back Pressure MPa 0.0~0.1
Screw Speed rpm 10~50
Vent Depth mm 0.02~0.08