Go to Main text Go to Main Menu

TRIEL® 5720

TPEE

Inquiry

TYPICAL DATA OF TRIEL® 5720 GRADE

PROPERTY UNIT ASTM METHOD TYPICAL DATA
Physical
Specific Gravity - D792 1.27
Water Absorption (24 hours at 23℃) % D570 0.4
Melt Flow Rate (230℃, 2.16kg) g/10min D1238 8.0
MECHANICAL
Tensile Strength at yield kgf/㎠ D638 450.0
Tensile Elongation at break % D638 >400
Flexural Strength at yield kgf/㎠ D790 215.0
Flexural Modulus kgf/㎠ D790 4800.0
Izod Impact Strength, notched, 23℃ (1/8”) kgf∙㎝/㎝ D256 No Break
Hardness (Shore D) Shore D 72.0
THERMAL
HDT, 4.6 ㎏f/㎠ 125.0
Vicat softening temperature 205.0
ELECTRICAL
OTHERS
UL-94 Flammability (1/16) - (UL 94) HB
※The figures listed in this table are typical values obtained under the standard test methods and may not be applicable for products that are under different application condition.

PROCESSING GUIDE FOR TRIEL® 5720 GRADE

General processing conditions for TRIEL® 5720 are shown below.
Drying prior to processing is essential to ensure desired appearance and property performance.

SPECIFICATION UNIT CONDITIONS
Drying Temperature 100~110
Drying Time hr 3~4
Moisture Content, Max % 0.02
Melt Temperature 220~240
Nozzle Temperature 220~240
Front Temperature 220~240
Middle Temperature 220~240
Rear Temperature 190~220
Mold Temperature 30~50
Back Pressure MPa 0.0~0.1
Screw Speed rpm 10~50
Vent Depth mm 0.02~0.08