TRIEL® 5652EM

TPEE

Inquiry

TYPICAL DATA OF TRIEL® 5652EM GRADE

PROPERTY UNIT ASTM METHOD TYPICAL DATA
Physical
Specific Gravity - D792 1.24
Water Absorption (24 hours at 23℃) % D570 0.5
Melt Flow Rate (230℃, 2.16kg) g/10min D1238 14
MECHANICAL
Tensile Strength at yield kgf/㎠ D638 350
Tensile Elongation at break % D638 >400
Flexural Strength at yield kgf/㎠ D790 165
Flexural Modulus kgf/㎠ D790 3,650
Izod Impact Strength, notched, 23℃ (1/8”) kgf∙㎝/㎝ D256 No Break
Hardness (Shore D) Shore D 65
THERMAL
HDT, 4.6 ㎏f/㎠ 117
Vicat softening temperature 200
ELECTRICAL
OTHERS
Mold Shrinkage (3mm thickness) % D955 1.7~2.0
※The figures listed in this table are typical values obtained under the standard test methods and may not be applicable for products that are under different application condition.

PROCESSING GUIDE FOR TRIEL® 5652EM GRADE

General processing conditions for TRIEL® 5652EM are shown below.
Drying prior to processing is essential to ensure desired appearance and property performance.

SPECIFICATION UNIT CONDITIONS
Drying Temperature 100~110
Drying Time hr 3~4
Moisture Content, Max % 0.02
Melt Temperature 220~250
Nozzle Temperature 220~250
Front Temperature 220~250
Middle Temperature 220~250
Rear Temperature 200~230
Mold Temperature 30~50
Back Pressure MPa 0.0~0.1
Screw Speed rpm 10~50
Vent Depth mm 0.02~0.08