TRIBIT® 1710

PBT

Inquiry

TYPICAL DATA OF TRIBIT® 1710 GRADE

PROPERTY UNIT ASTM METHOD TYPICAL DATA
Physical
Specific Gravity - D792 1.31
Water Absorption (24 hours at 23℃) % D570 0.1
Melt Flow Rate (260℃, 2.16kg) g/10min D1238 23
MECHANICAL
Tensile Strength at yield kgf/㎠ D638 450
Tensile Elongation at break % D638 100
Flexural Strength at yield kgf/㎠ D790 700
Flexural Modulus kgf/㎠ D790 25,000
Izod Impact Strength, notched, 23℃ (1/8”) kgf∙㎝/㎝ D256 4
THERMAL
HDT, 18.6 ㎏f/㎠ D648 57
ELECTRICAL
OTHERS
UL-94 Flammability - (UL 94) HB
Mold Shrinkage (3mm thickness) % D955 1.4 ~ 2.3
※The figures listed in this table are typical values obtained under the standard test methods and may not be applicable for products that are under different application condition.

PROCESSING GUIDE FOR TRIBIT® 1710 GRADE

General processing conditions for TRIBIT® 1710 are shown below.
Drying prior to processing is essential to ensure desired appearance and property performance.

SPECIFICATION UNIT CONDITIONS
Drying Temperature 120
Drying Time hr 3~5
Moisture Content, Max % 0.02
Melt Temperature 250~260
Nozzle Temperature 245~250
Front Temperature 250~260
Middle Temperature 245~255
Rear Temperature 235~245
Mold Temperature 60~80
Back Pressure MPa <70
Screw Speed rpm <60
Injection Pressure MPa <70
Injection Speed % <50
Hold Pressure MPa <50
Injection Cushion mm 3~6