TRILOY® TP260W

PC/ABS

문의하기

TYPICAL DATA OF TRILOY® TP260W GRADE

PROPERTY UNIT ASTM METHOD TYPICAL DATA
Physical
Specific Gravity - D792 1.30
Water Absorption (24 hours at 23℃) % D570 0.2
Melt Flow Rate (260℃, 2.16kg) g/10min D1238 18
MECHANICAL
Tensile Strength at yield kgf/㎠ D638 500
Tensile Elongation at break % D638 10
Flexural Strength at yield kgf/㎠ D790 750
Flexural Modulus kgf/㎠ D790 45,000
Izod Impact Strength, notched, 23℃ (1/8”) kgf∙㎝/㎝ D256 3
THERMAL
HDT, 18.6 ㎏f/㎠ D648 86
ELECTRICAL
OTHERS
UL-94 Flammability (1.4mm thickness) - (UL 94) V-0
Mold Shrinkage (3mm thickness) % D955 0.2~0.4
※The figures listed in this table are typical values obtained under the standard test methods and may not be applicable for products that are under different application condition.

PROCESSING GUIDE FOR TRILOY® TP260W GRADE

General processing conditions for TRILOY® TP260W are shown below.
Drying prior to processing is essential to ensure desired appearance and property performance.

SPECIFICATION UNIT CONDITIONS
Drying Temperature 80
Drying Time hr 3~4
Moisture Content, Max % 0.02
Melt Temperature 250~270
Nozzle Temperature 250~270
Front Temperature 250~270
Middle Temperature 240~265
Rear Temperature 230~250
Mold Temperature 40~80
Back Pressure MPa 0.4~0.6
Screw Speed rpm 50~60
Vent Depth mm 0.02~0.08
Injection Pressure MPa 50~80
Injection Speed % 20~50
Hold Pressure MPa 35~60
Injection Cushion mm 3~6