TRILOY® LU180

PC/PBT (Metallic)

문의하기

TYPICAL DATA OF TRILOY® LU180 GRADE

PROPERTY UNIT ASTM METHOD TYPICAL DATA
Physical
Specific Gravity - D792 1.19
Melt Flow Rate (250℃, 5kg) g/10min D1238 10
MECHANICAL
Tensile Strength at yield kgf/㎠ D638 500
Tensile Elongation at break % D638 100
Flexural Strength at yield kgf/㎠ D790 820
Flexural Modulus kgf/㎠ D790 20,000
Izod Impact Strength, notched, 23℃ (1/8”) kgf∙㎝/㎝ D256 55
THERMAL
HDT, 18.6 ㎏f/㎠ D648 105
ELECTRICAL
OTHERS
Mold Shrinkage (3mm thickness) % D955 0.5
※The figures listed in this table are typical values obtained under the standard test methods and may not be applicable for products that are under different application condition.

PROCESSING GUIDE FOR TRILOY® LU180 GRADE

General processing conditions for TRILOY® LU180 are shown below.
Drying prior to processing is essential to ensure desired appearance and property performance.

SPECIFICATION UNIT CONDITIONS
Drying Temperature 90~100
Drying Time hr 3~5
Moisture Content, Max % 0.02
Melt Temperature 260~280
Nozzle Temperature 250~270
Front Temperature 250~270
Middle Temperature 250~270
Rear Temperature 250~270
Mold Temperature 60~90
Back Pressure MPa <70
Screw Speed rpm <60
Injection Pressure MPa <70
Injection Speed % <50
Hold Pressure MPa <50
Injection Cushion mm 3~6