TRILOY® CF210M

PC/ABS

문의하기

TYPICAL DATA OF TRILOY® CF210M GRADE

PROPERTY UNIT ASTM METHOD TYPICAL DATA
Physical
Specific Gravity - D792 1.13
Water Absorption (24 hours at 23℃) % D570 0.2
Melt Flow Rate (260℃, 2.16kg) g/10min D1238 35
MECHANICAL
Tensile Strength at yield kgf/㎠ D638 600
Tensile Elongation at break % D638 60
Flexural Strength at yield kgf/㎠ D790 1,000
Flexural Modulus kgf/㎠ D790 26,000
Izod Impact Strength, notched, 23℃ (1/8”) kgf∙㎝/㎝ D256 7
Rockwell Hardness R scale D785 110
THERMAL
HDT, 18.6 ㎏f/㎠ D648 85
Coefficient of Linear Thermal Expansion ㎜/㎜/℃ D696 7.3 x 10-5
ELECTRICAL
Volume Resistivity Ω∙㎝ D257 5E+16
Dielectric Strength kV/㎜ D149 25
Dielectric Constant - D150 3
Dissipation Factor - D150 0.009
ARC Resistance sec D495 123
OTHERS
UL-94 Flammability (1.0mm thickness) - (UL 94) V-2
UL-94 Flammability (1.5mm thickness) V-0
Mold Shrinkage (3mm thickness) % D955 0.5~0.7
※The figures listed in this table are typical values obtained under the standard test methods and may not be applicable for products that are under different application condition.

PROCESSING GUIDE FOR TRILOY® CF210M GRADE

General processing conditions for TRILOY® CF210M are shown below.
Drying prior to processing is essential to ensure desired appearance and property performance.

SPECIFICATION UNIT CONDITIONS
Drying Temperature 100~110
Drying Time hr 3~5
Moisture Content, Max % 0.02
Melt Temperature 260~280
Nozzle Temperature 250~270
Front Temperature 255~275
Middle Temperature 255~275
Rear Temperature 245~265
Mold Temperature 60~90