TRICAP® OG14T

Organosheet

문의하기

TYPICAL DATA OF TRICAP® OG14T GRADE

PROPERTY UNIT TYPICAL DATA
Material - PP GF(Twill)
Fiber Contents Vol % 43.5
Specific Gravity - 1.62
Tensile Strength MPa 420
Tensile Modulus GPa 18.5
Flexural Strength MPa 430
Flexural Modulus GPa 18
Note -
※The figures listed in this table are typical values obtained under the standard test methods and may not be applicable for products that are under different application condition.

PROCESSING GUIDE FOR TRICAP® OG14T GRADE

Heating

  • Between 200℃ ~ 250℃
  • We recommend molding in the above temperature range for good impregnation performance and forming. It is recommended to use middle wavelength IR heater for heating heat source. Two-sided heating will be much more efficient than one side.

Pressing

  • 10 ~ 100 bar
  • The impregnation pressure may vary depending on the molded part, shape and molding tool.

Demolding Temperature

  • Under 100℃
  • It is recommended to demold at the lowest temperature possible to avoid deforming the shape during demolding process.

Dimensions

  • Precut on demand Plate, max size 600mm × 1500mm

Storage

  • The storage time of the Organosheet is infinite.

Handling

  • PP is stable at room temperature and normal pressure. In order to manufacture molded parts using Organosheet, you need a special safety guard and tools.