TRILOY® HF200S

PC/ABS

문의하기

TYPICAL DATA OF TRILOY® HF200S GRADE

PROPERTY UNIT ASTM METHOD TYPICAL DATA
Physical
Specific Gravity - D792 1.08
Water Absorption (24 hours at 23℃) % D570 0.12
Melt Flow Rate (260℃, 2.16kg) g/10min D1238 22
MECHANICAL
Tensile Strength at yield kgf/㎠ D638 450
Tensile Elongation at break % D638 80
Flexural Strength at yield kgf/㎠ D790 750
Flexural Modulus kgf/㎠ D790 24,000
Izod Impact Strength, notched, 23℃ (1/8”) kgf∙㎝/㎝ D256 60
THERMAL
HDT, 18.6 ㎏f/㎠ D648 82
ELECTRICAL
OTHERS
UL-94 Flammability (1.5mm thickness) - (UL 94) V-0, 5VA
Mold Shrinkage (3mm thickness) % D955 0.5~0.7
※The figures listed in this table are typical values obtained under the standard test methods and may not be applicable for products that are under different application condition.

PROCESSING GUIDE FOR TRILOY® HF200S GRADE

General processing conditions for TRILOY® HF200S are shown below.
Drying prior to processing is essential to ensure desired appearance and property performance.

SPECIFICATION UNIT CONDITIONS
Drying Temperature 80
Drying Time hr 3~4
Moisture Content, Max % 0.02
Melt Temperature 260~280
Nozzle Temperature 250~270
Front Temperature 255~275
Middle Temperature 255~275
Rear Temperature 245~265
Mold Temperature 60~90