TRIEL® 5300

TPEE

咨询

TYPICAL DATA OF TRIEL® 5300 GRADE

PROPERTY UNIT ASTM METHOD TYPICAL DATA
Physical
Specific Gravity - D792 1.10
Water Absorption (24 hours at 23℃) % D570 0.5
Melt Flow Rate (230도, 2.16kg) g/10min D1238 28
MECHANICAL
Tensile Strength at yield kgf/㎠ D638 130
Tensile Elongation at break % D638 >400
Flexural Strength at yield kgf/㎠ D790 23
Flexural Modulus kgf/㎠ D790 365
Izod Impact Strength, notched, 23℃ (1/8”) kgf∙㎝/㎝ D256 No Break
Hardness (Shore D) Shore D 30
THERMAL
HDT, 4.6 ㎏f/㎠ 52
Vicat softening temperature 108
ELECTRICAL
OTHERS
UL-94 Flammability (1/16") - (UL 94) HB
Mold Shrinkage % 1.8
※The figures listed in this table are typical values obtained under the standard test methods and may not be applicable for products that are under different application condition.

PROCESSING GUIDE FOR TRIEL® 5300 GRADE

General processing conditions for TRIEL® 5300 are shown below.
Drying prior to processing is essential to ensure desired appearance and property performance.

SPECIFICATION UNIT CONDITIONS
Drying Temperature 90~110
Drying Time hr 3~4
Moisture Content, Max % 0.02
Melt Temperature 180~210
Nozzle Temperature 180~210
Front Temperature 180~210
Middle Temperature 180~210
Rear Temperature 170~190
Mold Temperature 30~50
Back Pressure MPa 0.0~0.1
Screw Speed rpm 10~50
Vent Depth mm 0.02~0.08