TRIBIT® 1500G15K

PBT

咨询

TYPICAL DATA OF TRIBIT® 1500G15K GRADE

PROPERTY UNIT ASTM METHOD TYPICAL DATA
Physical
Specific Gravity - D792 1.43
Water Absorption (24 hours at 23℃) % D570 0.08
Melt Flow Rate (250℃, 5kg) g/10min D1238 68
MECHANICAL
Tensile Strength at yield kgf/㎠ D638 840
Tensile Elongation at break % D638 3
Flexural Strength at yield kgf/㎠ D790 1,300
Flexural Modulus kgf/㎠ D790 45,000
Izod Impact Strength, notched, 23℃ (1/8”) kgf∙㎝/㎝ D256 5
Rockwell Hardness R scale D785 119
THERMAL
HDT, 18.6 ㎏f/㎠ D648 195
Coefficient of Linear Thermal Expansion ㎜/㎜/℃ D696 3 x 10-5
ELECTRICAL
Volume Resistivity Ω∙㎝ D257 1E+16
Dielectric Strength kV/㎜ D149 21
Dielectric Constant - D150 3.2
Dissipation Factor - D150 0.02
ARC Resistance sec D495 150
OTHERS
UL-94 Flammability (0.75mm thickness) - (UL 94) HB
Mold Shrinkage (3mm thickness) % D955 0.2~1.2
※The figures listed in this table are typical values obtained under the standard test methods and may not be applicable for products that are under different application condition.

PROCESSING GUIDE FOR TRIBIT® 1500G15K GRADE

General processing conditions for TRIBIT® 1500G15K are shown below.
Drying prior to processing is essential to ensure desired appearance and property performance.

SPECIFICATION UNIT CONDITIONS
Drying Temperature 120
Drying Time hr 3~5
Moisture Content, Max % 0.02
Melt Temperature 250~270
Nozzle Temperature 245~265
Front Temperature 250~270
Middle Temperature 245~265
Rear Temperature 240~260
Mold Temperature 60~90