TYPICAL DATA OF TRAMID® 4110GNH35 GRADE
| PROPERTY | UNIT | ASTM METHOD | TYPICAL DATA |
|---|---|---|---|
| Physical | |||
| MECHANICAL | |||
| Tensile Strength at yield | kgf/㎠ | D638 | 1,450 |
| Tensile Elongation at break | % | D638 | > 1.5 |
| Flexural Strength at yield | kgf/㎠ | D790 | 1,950 |
| Flexural Modulus | kgf/㎠ | D790 | 89,500 |
| Izod Impact Strength, notched, 23℃ (1/8”) | kgf∙㎝/㎝ | D256 | 9.5 |
| THERMAL | |||
| HDT, 18.6 ㎏f/㎠ | ℃ | D648 | 207 |
| ELECTRICAL | |||
| OTHERS | |||
| UL-94 Flammability ((1.5mm)) | - | (UL 94) | V0 |
| Mold Shrinkage | % | 0.3~0.6 | |
※The figures listed in this table are typical values obtained under the standard test methods and may not be applicable for products that are under different application condition.
PROCESSING GUIDE FOR TRAMID® 4110GNH35 GRADE
General processing conditions for TRAMID® 4110GNH35 are shown below.
Drying prior to processing is essential to ensure desired appearance and property performance.
| SPECIFICATION | UNIT | CONDITIONS |
|---|---|---|
| Drying Temperature | ℃ | 80~120 |
| Drying Time | hr | 5~7 |
| Melt Temperature | ℃ | 240~260 |
| Nozzle Temperature | ℃ | 280~290 |
| Front Temperature | ℃ | 260~280 |
| Middle Temperature | ℃ | 240~260 |
| Rear Temperature | ℃ | 220~240 |
| Mold Temperature | ℃ | 60~80 |
| Back Pressure | MPa | <70 |
| Screw Speed | rpm | <60 |
| Injection Pressure | MPa | <70 |
| Injection Speed | % | <50 |
| Hold Pressure | MPa | <50 |
| Injection Cushion | mm | 3~6 |